标准：
符合GB SAI5183
相当 AWS ER5183
说明：
ER5183是含少量锰的铝镁合金焊丝，具有优良的抗裂性和耐蚀性，强度高。
ER5183 is an aluminum-magnesium alloy welding wire with a small amount of manganese, which has excellent crack resistance and corrosion resistance, and high strength.
用途：
适用于铝镁合金及铝锌镁合金的氩弧焊，是最常用的铝合金焊丝之一。
It is suitable for argon arc welding of aluminum-magnesium alloy and aluminum-zinc-magnesium alloy. It is one of the most commonly used aluminum alloy welding wires.
焊丝化学成分：
| Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Al |
| ≤0.40 | ≤0.40 | ≤0.10 | 0.50~0.10 | 4.3~5.2 | 0.05~0.25 | ≤0.25 | ≤0.15 | 余量 |
供应规格（mm）：
|
盘装Φ |
1.0 | 1.2 | 1.5 | 2.0 | 2.5 | ||
| 焊丝直径Φ（长度：1000） | 1.5 | 2.0 | 2.5 | 3.0 | 4.0 | 5.0 | 6.0 |
注意事项：
1. 焊前应严格清除工件焊接边缘及焊丝表面的氧化膜和油污等污物。
2. 施焊时可采用垫板托住熔化金属，以保证焊缝的成形。
3. 氧-乙炔气焊时必须配铝气焊熔剂共同使用。
1. Strictly remove the oxide film and oil stains on the welding edge of the workpiece and the surface of the welding wire before welding.
2. When welding, a backing plate can be used to hold the molten metal to ensure the formation of the weld.
3. Oxygen-acetylene gas welding must be used together with aluminum gas welding flux.
相关产品
S301 纯铝焊丝
铝及铝合金焊丝广泛用于铝及其合金氩弧焊及氧-乙炔气焊时作填充材料。氩弧焊是焊接铝及铝合金较完善的方法。氩弧焊可以不用熔剂，但氧-乙炔气焊时必须配铝气焊熔剂共同使用。焊丝的选择，主要根据母材的种类，对接头的抗裂性能，机械性能及抗腐蚀性能等方面的要求综合考虑。
ER4043 铝硅焊丝
铝及铝合金焊丝广泛用于铝及其合金氩弧焊及氧-乙炔气焊时作填充材料。氩弧焊是焊接铝及铝合金较完善的方法。氩弧焊可以不用熔剂，但氧-乙炔气焊时必须配铝气焊熔剂共同使用。焊丝的选择，主要根据母材的种类，对接头的抗裂性能，机械性能及抗腐蚀性能等方面的要求综合考虑。
ER4047 铝硅共晶合金焊丝
铝及铝合金焊丝广泛用于铝及其合金氩弧焊及氧-乙炔气焊时作填充材料。氩弧焊是焊接铝及铝合金较完善的方法。氩弧焊可以不用熔剂，但氧-乙炔气焊时必须配铝气焊熔剂共同使用。焊丝的选择，主要根据母材的种类，对接头的抗裂性能，机械性能及抗腐蚀性能等方面的要求综合考虑。
ER5183 铝镁焊丝
铝及铝合金焊丝广泛用于铝及其合金氩弧焊及氧-乙炔气焊时作填充材料。氩弧焊是焊接铝及铝合金较完善的方法。氩弧焊可以不用熔剂，但氧-乙炔气焊时必须配铝气焊熔剂共同使用。焊丝的选择，主要根据母材的种类，对接头的抗裂性能，机械性能及抗腐蚀性能等方面的要求综合考虑。
ER5356 铝镁焊丝
铝及铝合金焊丝广泛用于铝及其合金氩弧焊及氧-乙炔气焊时作填充材料。氩弧焊是焊接铝及铝合金较完善的方法。氩弧焊可以不用熔剂，但氧-乙炔气焊时必须配铝气焊熔剂共同使用。焊丝的选择，主要根据母材的种类，对接头的抗裂性能，机械性能及抗腐蚀性能等方面的要求综合考虑。
在线咨询
0511-86738080 
点击咨询 