Z508 镍铜铸铁焊条
标准：
符合GB EZNiCu-1
相当AWS ENiCu-B
说明：
Z508是镍铜合金（蒙乃尔）焊芯，强还原性石墨型药皮的铸铁焊条。可交直流两用，电弧稳定，操作方便。焊缝金属较软但颜色比较亮，收缩率大，抗裂性比较差，焊缝强度也不高，故不宜用于受力部位和对新铸件有色差要求的焊补。为了防止裂缝，对被焊母材推荐采用150~300℃低温预热，以减小焊接应力。
Z508 is a nickel-copper alloy (Monel) core, cast iron electrode with strong reducing graphite coating. It can be used for both AC and DC, with stable arc and convenient operation. The weld metal is soft but the color is brighter, the shrinkage rate is large, the crack resistance is relatively poor, and the weld strength is not high, so it is not suitable for welding repairs on stressed parts and new castings with chromatic aberration requirements. In order to prevent cracks, it is recommended to use 150~300℃ low temperature preheating for the base material to be welded to reduce welding stress.
用途：
常用于强度要求不高的灰口铸铁气孔及砂眼的补焊。
It is often used for repair welding of gray cast iron pores and blisters with low strength requirements.
熔敷金属化学成分（%）
| C | Si | Mn | Ni | Cu | Fe | S |
| ≤1.0 | ≤0.80 | ≤2.50 | 60.0~70.0 | 25.0~35.0 | ≤6.0 | ≤0.025 |
参考电流：AC或DC
| 焊条直径（mm） | 3.2 | 4.0 | 5.0 |
| 焊接电流（A） | 80~100 | 110~140 | 150~180 |
注意事项：
1. 首先清除焊接部位的油污、砂、水、锈等污物，并视缺陷类型，开坡口、打止裂孔及熔池造型等准备措施。
2. 如填补大的空隙，应先从四周开始堆焊一层，然后向中部逐步填满。
3. 为避免母材熔化过多，减少白口层。施焊中，尽量采用小电流，短。，短道，分散分段焊，每段焊道长度一般不超过50mm，待温度降至不烫手时再继续施焊。并且施焊后立即锤击焊缝以松驰应力防止裂纹。
4. 施焊前应将焊条在150℃左右烘焙一小时。
1. First, remove oil, sand, water, rust and other contaminants from the welding part, and prepare measures such as beveling, cracking prevention, and molten pool modeling depending on the type of defect.
2. To fill a large gap, start from the surrounding area by surfacing one layer, and then gradually fill it up to the middle.
3. In order to avoid excessive melting of the base material, reduce the white mouth layer. In welding, try to use small current, short arc, narrow track, short track, dispersed segment welding, the length of each segment of the weld generally does not exceed 50mm, and continue welding when the temperature drops to not hot. And immediately after welding, hammer the weld to relax the stress and prevent cracks.
4. The welding rod should be baked at about 150℃ for one hour before welding.
相关产品
白铜焊条Cu307
Z308 纯镍铸铁焊条
焊补铸铁用的镍基铸铁焊条在铸铁焊接中属于异质焊缝的冷态焊焊条。药皮为强还原性石墨型，交直流两用，工艺性能良好，可全位置焊接。焊缝金属不存在硬而脆的CFe3（渗碳体）即白口组织，所以焊缝金属具有良好的加工性和承受塑性变形的能力。但熔合区由于母材成分熔化的影响，仍不可避免地会有不同程度的白口组织。为了减轻熔合区硬脆组织对焊后加工性能的不良影响，使其白口层尽量较少，较薄、且不连续，施焊时应该严格遵循冷焊工艺规定操作。另外，某些铸件（如长期在高温、水蒸气中工作的炉栅，锅炉等），因其中的碳已被烧损，铸件具有多空性，变得十分松脆而无法焊、补。
Z408 镍铁铸铁焊条
焊补铸铁用的镍基铸铁焊条在铸铁焊接中属于异质焊缝的冷态焊焊条。药皮为强还原性石墨型，交直流两用，工艺性能良好，可全位置焊接。焊缝金属不存在硬而脆的CFe3（渗碳体）即白口组织，所以焊缝金属具有良好的加工性和承受塑性变形的能力。但熔合区由于母材成分熔化的影响，仍不可避免地会有不同程度的白口组织。为了减轻熔合区硬脆组织对焊后加工性能的不良影响，使其白口层尽量较少，较薄、且不连续，施焊时应该严格遵循冷焊工艺规定操作。另外，某些铸件（如长期在高温、水蒸气中工作的炉栅，锅炉等），因其中的碳已被烧损，铸件具有多空性，变得十分松脆而无法焊、补。
Z508 镍铜铸铁焊条
焊补铸铁用的镍基铸铁焊条在铸铁焊接中属于异质焊缝的冷态焊焊条。药皮为强还原性石墨型，交直流两用，工艺性能良好，可全位置焊接。焊缝金属不存在硬而脆的CFe3（渗碳体）即白口组织，所以焊缝金属具有良好的加工性和承受塑性变形的能力。但熔合区由于母材成分熔化的影响，仍不可避免地会有不同程度的白口组织。为了减轻熔合区硬脆组织对焊后加工性能的不良影响，使其白口层尽量较少，较薄、且不连续，施焊时应该严格遵循冷焊工艺规定操作。另外，某些铸件（如长期在高温、水蒸气中工作的炉栅，锅炉等），因其中的碳已被烧损，铸件具有多空性，变得十分松脆而无法焊、补。
Cu107 紫铜焊条
铜及铜合金焊条用途较广，除了用紫铜焊条焊接紫铜外，目前采用较多的是用青铜焊条来焊接铜及铜合金、铜与钢等。但铜及其合金的弧焊一般较钢困难。这是由于铜及铜合金焊接时易产生金属氧化、元素烧损、以及气孔、裂缝和变形等。另外，铜及其合金的导热性特别高致使焊条在引弧后往往不能使母材熔融，而产生熔滴飞散，故焊接铜及铜合金时该类焊件焊前必须要有合理的预热及用较大的焊接电流、直流反接，短弧垂直。焊后应对焊缝进行适当锤击，以消除应力及细化晶粒。另外，铜及其合金塑性好且不溶解碳，也不与碳化合生成脆硬组织，故铜及铜合金焊条也能用来焊补铸铁。