标准：
符合GB EDCoCr-B-03
相当AWS ECoCr-B
说明：
D812是钛钙型药皮，中碳的钴铬钨合金为焊芯的堆焊焊条。可交直流两用，电弧稳定，渣复盖性好，成型美观。堆焊层具有良好的耐蚀及耐磨性能，在600℃以上的高温中也能保持这种特性。D812在钴铬钨堆焊合金中具有中等硬度，耐磨性较D802好，但塑性较D802稍差。用硬质合金刀具可进行切削加工。金相组织为奥氏体和共晶体。
D812 is a titanium-calcium type coating, a medium-carbon cobalt-chromium-tungsten alloy surfacing electrode with a core. It can be used for both AC and DC, stable arc, good slag coverage, and beautiful shape. The surfacing layer has good corrosion resistance and wear resistance, and can maintain this characteristic even at high temperatures above 600°C. D812 has medium hardness among cobalt-chromium-tungsten surfacing alloys, and its wear resistance is better than D802, but its plasticity is slightly worse than D802. Carbide cutting tools can be used for cutting. The metallographic structure is austenite and eutectic.
用途：
用于高温高压阀门，内燃机阀、化纤剪切刀刃口、高压泵的轴套筒和内衬套筒、热轧型孔等堆焊。
Used for surfacing welding of high temperature and high pressure valves, internal combustion engine valves, chemical fiber shear blades, shaft sleeves and lining sleeves of high pressure pumps, and hot rolled holes.
熔敷金属化学成分（%）
| C | Mn | Si | Cr | W | Co | Fe | 其他元素总量 |
| 1.0~1.70 | ≤2.0 | ≤2.0 | 25.0~32.0 | 7.0~10.0 | 余量 | ≤5.0 | ≤4.0 |
堆焊层常温硬度值
HRc=45~50
以上化学成分及常温硬度指堆焊三层以上堆焊金属。
The above chemical composition and normal temperature hardness refer to the surfacing welding of more than three layers of surfacing metal.
参考电流：AC或DC
| 焊条直径（mm） | 3.2 | 4.0 | 5.0 |
| 焊接电流（A） | 90~130 | 140~170 | 170~200 |
注意事项：
1. 焊前焊条须经150℃烘焙一小时。
2. 为了避免产生裂缝，根据工件大小和母材种类，须经过200~400℃的预热。并宜采用小电流短弧焊接。焊后应将工件立即放入干燥和预热的砂缸或草灰中缓冷。
3. 由于电弧焊的温度较气焊高，故稀释率也较气焊大，因此一般只在难于进行气焊或为提高焊接效率时才考虑电弧焊。
1. The electrode must be baked at 150℃ for one hour before welding.
2. In order to avoid cracks, according to the size of the workpiece and the type of base material, it must be preheated at 200~400℃. And it is advisable to use small current short arc welding. After welding, the workpiece should be placed in a dry and preheated sand jar or straw ash to cool slowly.
3. Since the temperature of arc welding is higher than that of gas welding, the dilution rate is also greater than that of gas welding. Therefore, arc welding is generally only considered when it is difficult to perform gas welding or to improve welding efficiency.
相关产品
白铜焊条Cu307
Z308 纯镍铸铁焊条
焊补铸铁用的镍基铸铁焊条在铸铁焊接中属于异质焊缝的冷态焊焊条。药皮为强还原性石墨型，交直流两用，工艺性能良好，可全位置焊接。焊缝金属不存在硬而脆的CFe3（渗碳体）即白口组织，所以焊缝金属具有良好的加工性和承受塑性变形的能力。但熔合区由于母材成分熔化的影响，仍不可避免地会有不同程度的白口组织。为了减轻熔合区硬脆组织对焊后加工性能的不良影响，使其白口层尽量较少，较薄、且不连续，施焊时应该严格遵循冷焊工艺规定操作。另外，某些铸件（如长期在高温、水蒸气中工作的炉栅，锅炉等），因其中的碳已被烧损，铸件具有多空性，变得十分松脆而无法焊、补。
Z408 镍铁铸铁焊条
焊补铸铁用的镍基铸铁焊条在铸铁焊接中属于异质焊缝的冷态焊焊条。药皮为强还原性石墨型，交直流两用，工艺性能良好，可全位置焊接。焊缝金属不存在硬而脆的CFe3（渗碳体）即白口组织，所以焊缝金属具有良好的加工性和承受塑性变形的能力。但熔合区由于母材成分熔化的影响，仍不可避免地会有不同程度的白口组织。为了减轻熔合区硬脆组织对焊后加工性能的不良影响，使其白口层尽量较少，较薄、且不连续，施焊时应该严格遵循冷焊工艺规定操作。另外，某些铸件（如长期在高温、水蒸气中工作的炉栅，锅炉等），因其中的碳已被烧损，铸件具有多空性，变得十分松脆而无法焊、补。
Z508 镍铜铸铁焊条
焊补铸铁用的镍基铸铁焊条在铸铁焊接中属于异质焊缝的冷态焊焊条。药皮为强还原性石墨型，交直流两用，工艺性能良好，可全位置焊接。焊缝金属不存在硬而脆的CFe3（渗碳体）即白口组织，所以焊缝金属具有良好的加工性和承受塑性变形的能力。但熔合区由于母材成分熔化的影响，仍不可避免地会有不同程度的白口组织。为了减轻熔合区硬脆组织对焊后加工性能的不良影响，使其白口层尽量较少，较薄、且不连续，施焊时应该严格遵循冷焊工艺规定操作。另外，某些铸件（如长期在高温、水蒸气中工作的炉栅，锅炉等），因其中的碳已被烧损，铸件具有多空性，变得十分松脆而无法焊、补。
Cu107 紫铜焊条
铜及铜合金焊条用途较广，除了用紫铜焊条焊接紫铜外，目前采用较多的是用青铜焊条来焊接铜及铜合金、铜与钢等。但铜及其合金的弧焊一般较钢困难。这是由于铜及铜合金焊接时易产生金属氧化、元素烧损、以及气孔、裂缝和变形等。另外，铜及其合金的导热性特别高致使焊条在引弧后往往不能使母材熔融，而产生熔滴飞散，故焊接铜及铜合金时该类焊件焊前必须要有合理的预热及用较大的焊接电流、直流反接，短弧垂直。焊后应对焊缝进行适当锤击，以消除应力及细化晶粒。另外，铜及其合金塑性好且不溶解碳，也不与碳化合生成脆硬组织，故铜及铜合金焊条也能用来焊补铸铁。